We are professional manufacturer of alumina ceramic products.
We have focused on ceramic products for more than 20 years since year 1994.
Our ceramic products include ceramic insulator, ceramic pipe/tube,ceramic rod, textile ceramics,etc.
If you have any inquiry,please offer drawing, sample or dimension.
We can customise it for you and choose the best suitable material for your request and application.
Parameters of alumina ceramics:
Â
Material
Unit
Steatite ceramics
95% alumina ceramics
99.5% alumina ceramics
Density
G/cm3
2.7
3.65
3.85
Highest application temperature
°C
1100
1500
1800
Bending strength
Mpa
150
300
340
Compressive strength
Mpa
900
3400
3600
Hardness
HV0.5
800
1800
2000
Insulation breakdown strength
KV/mm
10
15
18
Accuracy of working(mm)
Perpendicularity
0.01
Concentricity
0.01
Roundness
0.005
Straightness
0.005
Parallelism
0.01
Planeness
0.005
Roughness
0.05
Fit clearance
0.005
Ceramic eyelet apply to the coiling machine and spinning and weaving machinery, is in common use fault silk another piece, is used to demand no high fault silk occasion. Silk thread slides when the job, in China eye outside, for reducing friction, must raise material hardness, smoothness and form. Our company selects and uses 99%'s Al2O3, hardness greater than HRa88, density 3.85, surpasses essence throwing Ra0.2.
Introduction:
We are professional manufacturer of alumina ceramic products.
We have focused on ceramic products for more than 20 years since year 1994.
Our ceramic products include ceramic insulator, ceramic pipe/tube,ceramic rod, textile ceramics,etc.
If you have any inquiry,please offer drawing, sample or dimension.
We can customise it for you and choose the best suitable material for your request and application.
Parameters of alumina ceramics:
Â
Material
Unit
Steatite ceramics
95% alumina ceramics
99.5% alumina ceramics
Density
G/cm3
2.7
3.65
3.85
Highest application temperature
°C
1100
1500
1800
Bending strength
Mpa
150
300
340
Compressive strength
Mpa
900
3400
3600
Hardness
HV0.5
800
1800
2000
Insulation breakdown strength
KV/mm
10
15
18
Accuracy of working(mm)
Perpendicularity
0.01
Concentricity
0.01
Roundness
0.005
Straightness
0.005
Parallelism
0.01
Planeness
0.005
Roughness
0.05
Fit clearance
0.005
Ceramic eyelet apply to the coiling machine and spinning and weaving machinery, is in common use fault silk another piece, is used to demand no high fault silk occasion. Silk thread slides when the job, in China eye outside, for reducing friction, must raise material hardness, smoothness and form. Our company selects and uses 99%'s Al2O3, hardness greater than HRa88, density 3.85, surpasses essence throwing Ra0.2.
Textile Ceramic Eyelet for Wire Guiding
Model NO.: Textile Ceramic
Processing Trade: Processing with Imort Material
Certification: CE, ISO9001: 2000, TUV
Customized: Customized
Condition: Used
Refractoriness (ºC): 1580< Refractoriness< 1770
Type: Refractory Material
Content of Alumina: 99, 95, 90, 85
Bulk Density: >3.85g/cm3
Fracture Toughness: 2.5MPa.M1/2
Application: Electronics, Metallurgy
Feature: Long Time Materials
Temperature: 1650 Degree C
Compressive Strength: >300MPa
Absorption: 0.05%
Trademark: Heatfounder
Transport Package: Standard Safe Carton or Pallet
Specification: high alumina ceramic
Origin: Shanghai
HS Code: 8547100000
Model NO.: Textile Ceramic
Processing Trade: Processing with Imort Material
Certification: CE, ISO9001: 2000, TUV
Customized: Customized
Condition: Used
Refractoriness (ºC): 1580< Refractoriness< 1770
Type: Refractory Material
Content of Alumina: 99, 95, 90, 85
Bulk Density: >3.85g/cm3
Fracture Toughness: 2.5MPa.M1/2
Application: Electronics, Metallurgy
Feature: Long Time Materials
Temperature: 1650 Degree C
Compressive Strength: >300MPa
Absorption: 0.05%
Trademark: Heatfounder
Transport Package: Standard Safe Carton or Pallet
Specification: high alumina ceramic
Origin: Shanghai